There are three main forms of Casting Mold failure

1 thermal fatigue crack damage failure

Thermal fatigue cracking failure of die casting production, mold repeatedly stimulated cooling and heating effect, the molding surface and internal deformation are involved, and the repeated cycles of thermal stress, leading to tissue structure of two injury and loss of toughness, causing cracks appeared, and continue to expand, once a crack expanding, and molten metal liquid impact, coupled with repeated mechanical stress crack accelerated expansion. Therefore, on one hand casting mold must be fully preheat starting. In addition, in the production of the die casting die in must be kept in a certain temperature range, so as to avoid the early cracking. At the same time, to ensure the mold production and manufacturing of internal no problem. Because of the practical production, the majority of the ineffectiveness of the die thermal fatigue cracking. Read more